Ebeam – Conductive Substrate

Ebeam lithography at 100kV can only be performed on electrically conductive substrates, or on substrates coated with a thin conductive layer of metal properly grounded to the sample holder.

The schematic drawing below illustrates some of the most common grounding schemes, as well as several of the most likely mistakes. The principle is simple – there must always exist a conductive path for the incident electrons to travel all the way to the sample holder, which itself is properly grounded by the tool. Any non-conductive obstacle will result in charging problems. 

The energy in the lithographic electron beam can be as much as million times higher than it is on the SEM set up to image poorly conductive samples. Trouble starts if this energy does not have a chance to be properly and immediately dissipated. The severity of the problem and its  consequences will depend on the actual setup. They can be relatively mild, but there exists a serious potential for a physical damage to the tool and several weeks of downtime.

How bad can things get?

Relatively good scenario – small charging

Even in cases where everything was setup correctly, small amount of charging can be present. Most ebeam resists are insulators, and if they are the top surface layer, however thin, some charging will happen there. Depending on the resist, current, pattern density, writing speed and writing order, several nanometers or even tens of nanometers of beam displacement and pattern placement errors can result. The mask-making industry  had to introduce conductive polymer top-coat and other writing order modifications already around 65nm technology node for certain mask designs to meet the ITRS roadmap image placement specifications. 

Bad scenario – strong charging

When charging gets stronger, the lithography suffers. Image placement errors become noticeable, commonplace, and often the patterns disappear altogether as the beam gets deflected by the strong surface charge. Here is an example of what can happen during an exposure on a non-conductive substrate with properly deposited thin metallic layer, that unfortunately failed to get grounded properly. Substrate – glass, coated properly with thin layer of Ti+Al, resist HSQ.

The thin conductive film got saturated with charge very fast, and once it did, the resulting charge deflected the beam all over the writing field. The charge only got a chance to dissipate little bit during the field-to-field stage move delay, resulting in a repetitive pattern of disorderly lithography. Image courtesy of Karim Achouri and Kevin Mueller.

Catastrophic scenario

If one simply coats a glass substrate with a polymer resist and starts an exposure with high enough current, dense pattern and high enough dose – really bad things will happen really fast. The massive accumulated energy will instantly increase the substrate surface temperature above the resist melting point, there will be an explosion of micro-droplets of resist into all direction. If one of those droplets finds its way into the objective lens, it will be game over for any lithography, as the beam will now charge and drift, until the column gets opened and cleaned (all affected parts replaced) – potentially several weeks of downtime.

In case the substrate is not only insulating, but also pyroelectric (for example lithium niobate), there also exists a potential for some of the detectors and electronics inside of the tool being knocked-out by an induced surface discharge.